synchrotron X-ray scattering and nanoindentation testIm, S.*; Jee, H.*; Suh, H.*; 兼松 学*; 諸岡 聡; Choe, H.*; 西尾 悠平*; 町田 晃彦*; Kim, J.*; Lim, S.*; et al.
Construction and Building Materials, 365, p.130034_1 - 130034_18, 2023/02
被引用回数：6 パーセンタイル：67.49(Construction & Building Technology)Nanocrystalline calcium-silicate-hydrate (C-S-H) is a typical heterogeneous material with a multiscale structure spanning a wide length scale from angstrom to micrometer, and whose structure is determined by the Ca/Si ratio. In this study, we directly applied compressive loads on synthetic C-S-H pastes with Ca/Si ratios of 0.6-1.2 and investigated their mechanical properties using the elastic modulus calculated at three length scale levels (i.e., angstrom to nanometer, micrometer, and millimeter) via in-situ synchrotron X-ray scattering, nanoindentation tests, and strain gauges, respectively. Further, 
Si nuclear magnetic resonance spectroscopy was conducted on the C-S-H pastes to elucidate the alterations in the silicate polymerization. The experimental results confirmed the deformation behavior of the C-S-H paste with different Ca/Si ratios under external loading, which was demonstrated to be transferred from the surface of the pastes to particles owing to the presence of multiscale pores.
Kim, G.*; Im, S.*; Jee, H.*; Suh, H.*; Cho, S.*; 兼松 学*; 諸岡 聡; 小山 拓*; 西尾 悠平*; 町田 晃彦*; et al.
Cement and Concrete Research, 159, p.106869_1 - 106869_17, 2022/09
被引用回数：18 パーセンタイル：91.76(Construction & Building Technology)This study explored the effect of M-S-H formation on the local atomic arrangements and mechanical properties of C-S-H. The elastic moduli of the samples were calculated using shifted atomic distances (r) and d-spacings (d) acquired by applying an external load on the pastes during X-ray scattering experiments. The experimental results indicated that the crystal structure of C-S-H remained intact with MgCl
addition. At the highest Mg/Si ratio (Ca/Si = 0.6, Mg/Si = 0.2), change in the dominant phase occurred from C-S-H to M-S-H because the low pH environment hindered the formation of C-S-H and facilitated the formation of M-S-H. The elastic modulus decreased with increasing Mg/Si ratio up to 0.1 owing to both C-S-H destabilization and low M-S-H content in the samples. Conversely, the elastic modulus increased in the paste synthesized with the highest Mg/Si ratio because considerable M-S-H had formed, which exhibited a higher elastic modulus than C-S-H.
Im, S.*; Jee, H.*; Suh, H.*; 兼松 学*; 諸岡 聡; 小山 拓*; 西尾 悠平*; 町田 晃彦*; Kim, J.*; Bae, S.*
Journal of the American Ceramic Society, 104(9), p.4803 - 4818, 2021/09
被引用回数：18 パーセンタイル：84.26(Materials Science, Ceramics)This study aims to elucidate the effect of heating on the local atomic arrangements, structure, phase transformation, and mechanical properties of synthesized calcium-silicate-hydrate (C-S-H). The alteration in the atomic arrangement of the synthesized C-S-H (Ca/Si = 0.8) and the formation of crystalline phases that occurred in three distinct transformation stages of dehydration (105-200 
C), decomposition (300-600 C), and recrystallization (700-1000 C) were investigated via powder X-ray diffraction, Si nuclear magnetic resonance spectroscopy, and thermogravimetric analysis. Further, the deformation of the local atomic bonding environment and variations in mechanical properties during the three stages were assessed via pair distribution function analysis based on in-situ total X-ray scattering. The results revealed that the C-S-H paste before heating exhibited a lower elastic modulus in real space than that in the reciprocal space in the initial loading stage because water molecules acted as a lubricant in the interlayer. At the dehydration stage, the strain as a function of external loading exhibited irregular deformation owing to the formation of additional pores induced by the evaporation of free moisture. At the decomposition stage, the structural deformation of the main d-spacing (d 
3.0 
) was similar to that of the real space before the propagation of microcracks. At the recrystallization stage, the elastic modulus increased to 48 GPa owing to the thermal phase transformation of C-S-H to crystalline 
-wollastonite. The results provide direct experimental evidence of the micro- and nanostructural deformation behavior of C-S-H pastes after exposure to high temperature under external loading.